The RINA FH36 shipbuilding steel plates have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). RINA FH36 shipbuilding steel plate can achieve the impact toughness at Celsius degree -60°. All the RINA FH36 shipbuilding steel plate offered by Katalor Industry can be certificated by Registro Italiano Navale (RINA) as per customer’s request.
RINA FH36 Shipbuilding steel plates are mainly used for making the offshore oil drilling platform, the hull of ship building and ship repairing, the platform pipe joints and other components.
| Grade |
C % |
Si % |
Mn % |
P % |
S % |
V % |
AL % |
Cr % |
|
RINA Grade FH36 |
0.160 |
0.1-0.5 |
0.90-1.6 |
0.025 |
0.025 |
0.05-0.10 |
0.015 |
0.200 |
|
Cu % |
Mo % |
Nb % |
Ni % |
Ti % |
N% |
|
|
|
|
0.350 |
0.080 |
0.02-0.05 |
0.400 |
0.020 |
0.009 |
|
|
| Grade |
Thickness(mm) |
MinYield(Mpa) |
Tensile(Mpa) |
Elongation (%) |
Min Impact Energy |
|
|
RINA Grade FH36 |
8mm-50mm |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
34J |
|
51mm-70mm |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
41J |
|
|
71mm-100mm |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
50J |
|
|
The min impact energy is longitudinal energy |
||||||
| Thickness |
3-150mm |
|
Width |
1220-4200mm |
|
Length |
5000-18000mm |
Notes: coil thickness ≤ 25mm
RINA FH36 shipbuilding steel plateis a kind of high tensile strength marine steel. As with other grades of steel, they have a specific gravity of 7.8.RINA FH36 Shipbuilding steel plates also can be used for producing container and bulk cargo vessels as well as cruise ships, ferries and yachts. Please contact katalor if you wan to know more information of RINA FH36 Shipbuilding steel plate.