Home >SAE J403 >SAE J403 SAE1008 steel work / steel structure / steel machining parts
SAE J403 SAE1008 steel work / steel structure / steel machining  parts

SAE J403 SAE1008 steel work / steel structure / steel machining parts

SAE 1008 steel work Applications: AISI 1008 low carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.
0086-21-61182423
[email protected]
PDF Download
Live Chat  Leave a Message

SAE1008 steel contains very low carbon so it is called low carbon steel. It is suitable for the stamping and cold forming.

We keep more than 1000 ton SAE1008 steel stock. Based on the stock, we can produce many specifications of SAE1008 steel work / steel structure / steel machining parts based on the customer's requirement.

The following datasheet will provide more details about SAE 1008 steel work .

SAE 1008 steel work chemical composition

Element

Content (%)

Iron, Fe

99.31-99.7 %

Manganese, Mn

0.30-0.50 %

Carbon, C

0.10 %

Sulfur, S

0.050 %

Phosphorous, P

0.040 %

SAE 1008 steel structure physical properties

Properties

Metric

Imperial

Density (composition 0.06% C, 0.38% Mn, 0.01% Si, annealed at 925°C)

7.872 g/cm3

0.2844 lb/in³

SAE 1008 steel apare parts mechanical properties

Properties

Metric

Imperial

Tensile strength

340 MPa

49300 psi

Yield strength (depending on temper)

285 MPa

41300 psi

Elastic modulus

190-210 Gpa

27557-30458 ksi

Bulk modulus (typical for steel)

200 GPa

29000 ksi

Shear modulus (typical for steel)

80.0 GPa

11600 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (in 50 mm)

20%

20%

Reduction of area

45%

45%

Hardness, Brinell

95

95

Hardness, Knoop (converted from Brinell hardness)

113

113

Hardness, Rockwell B (converted from Brinell hardness)

55

55

Hardness, Vickers (converted from Brinell hardness)

98

98

Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)

55

55

SAE 1008 steel structure thermal properties are tabulated below

Properties

Metric

Imperial

Thermal expansion co-efficient (@0.000-100°C/32-212°F)

12.6 µm/m°C

7 µin/in°F

Thermal conductivity (composition of 0.06% C, 0.4% Mn; 0°C )

65.2 W/mK

452 BTU in/hr.ft².°F

SAE 1008 steel work Applications

AISI 1008 low carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.

SAE 1008 steel machining parts Production technology

Drilling, cutting, bending, welding, groove, correction, edge processing, spraying assembly etc.

Shanghai Katalor has been engaged in the steel work industry for many years. We have much experience in fabricating the SAE 1008 steel work / steel structure / steel machining parts. If you have the demand for this products, please contact us.

  • SAE J403 SAE1020 steel work / steel structure / steel machining parts

  • SAE J403 SAE1006 steel work / steel structure / steel machining parts

  • SAE J403 SAE1010 steel work / steel structure / steel machining parts

Contact Us

Shanghai Katalor Enterprises Co., Ltd

0086-21-61182423
0086-21-61182425
[email protected]
No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China
Live Chat

Project