Corten B under ASTM Weathering Steel plate’s Copper Brittle Defect Control

Corten B under ASTM Weathering Steel plate’s Copper Brittle Defect Control

The general precautions for copper brittleness of ASTM Corten B weathering steel plate are:

 

1. Optimization of heating process and reasonable sequencing can avoid the accumulation and accumulation of copper in ASTM Corten B weathering steel during heating, thus reducing the occurrence of copper brittle defects.

2. Furnace time has a great influence on the copper brittleness of ASTM Corten B weathering steel. The longer the furnace time, the more favorable the diffusion of copper along the grain boundary, and the easier it is to form cracks like cracks or bubbles like copper brittleness. The data shows that the furnace temperature is generally controlled within 360 min, which is more suitable. When the furnace time is > 360min, the thin gauge product should be modified. Otherwise, the slab should be removed and withdrawn.

3 The temperature should be controlled at <1210 ° C or higher than 1280 ° C. When the oven temperature is 1210-1280 ° C, the order of thickness is preferably less than 3.3 mm.

 

 Katalor is a famous supplier of ASTM Corten B weathering steel plate in China and our factory is very strong. Can meet your special requirements of ASTM Corten B weathering steel plate. If you need , Katalor alsod can supply additional processing about ASTM Corten B weathering steel plate. Welcome to send inquiry of ASTM Corten B weathering steel plate to katalor.

 

Pre: Popular ASTM A572 Grade 50 low alloy steel’s Alloying elements

Next: The way to remove the corrosion of GBT 8162 42CrMo seamless steel pipe

Contact Us

Shanghai Katalor Enterprises Co., Ltd

0086-18317160019
[email protected]
No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China
Live Chat