16Mo3 steel plate for boiler and pressure vessel

16Mo3 steel plate for boiler and pressure vessel

Introduction of 16Mo3 steel plate:

16MO3 steel plate is a foreign brand steel plate, which is used to make boilers and pressure vessels. It is different from other raw materials during welding. It must be preheated first, and the weld should be kept warm for about 30 minutes after the welding is completed. 16MO3 manganese steel plate is also an important alloying element of steel, it is an important hardenability element, and it has a great influence on the patience of the weld metal.

16Mo3 executive standard is: European standard EN10028-2.

Mechanical properties of 16Mo3 steel plate:

Yield strength R/MPa: ≥260

Tensile strength R/MPa: 440-490

Elongation after break (%): ≥22

Shock temperature (℃): 20

Impact energy minimum value (J): 31

Chemical composition of 16Mo3 steel plate:

C (0.12-0.20) Si (≤0.35) Mn (0.40-0.90) P (≤0.025)

S (≤0.01) Cu (≤0.3) Ni (≤0.3) Cr (≤0.3) Al (≥0.02)

N (≤0.012)

16Mo3 steel plate features:

Heat resistance and corrosion resistance.

When the Mn content is less than 5%, the patience of the weld metal is very high;

When the Mn content is greater than 3%, it is very brittle;

When the Mn content is between 60% and 180%, the weld metal has higher strength and resistance.

Pre: SAPH440 steel: Chemical Composition and Mechanical Properties

Next: What is S690QL equivalent Chinese standard?

Contact Us

Shanghai Katalor Enterprises Co., Ltd

0086-18317160019
[email protected]
No.230,1st Floor,Building No.1,No.221 Of Huashen Road,Free Trade Area Of Pudong New District,Shanghai China
Live Chat